A new type of hot-rolled transformation induced plasticity (TRIP) steel with 2.3%Al was developed to replace conventional Si-bearing TRIP steel to improve surface quality of the steel sheet. The relationship between retained austenite volume fraction and hot-rolling processing was researched by Gleeble-2000 thermo-dynamic test for the Al-bearing steel. The experimental result showed that aluminum played an important role on retaining austenite and the volume fraction increased from 4.4% to 7.5% as coiling temperature increased from 350℃ to 450℃, while coiling temperature had a stronger effect on retaining austenite than finishing rolling temperature.
关键词:
Aluminum
,
retained
,
austenite
,
coiling
,
temp
Yu CHEN
材料科学技术（英）
strength of 775 MPa, high elongation of 29% and low ductile-brittle transmission temperature less than -80℃ has been developed in laboratory based on the common silicon and manganese chemical composition. The experimental results showed that the microstructures were featured with ultra fine grain size less than 5 μm, appropriate retained austenite volume fraction around 11.8% and purified ferrite grain, which may result in well balanced mechanical properties for the steel.
关键词:
Ultra fine grain
,
null
,
null
,
null
,
null